CONTENTS |
100% ACRYLIC HOMOPOLYMER |
INTERNAL TISSUE |
ACRYLIC |
WEIGHT |
525 g/m² ± 5% |
AIR PERMEABILITY |
9.000 – 11.000 lt/dm²/hour (Dp:200 Pa) |
THICKNESS |
2.0mm |
BREAKING STRENGTH |
Longitudinal: 110 kgf/5 cm - Transverse: 140 kgf/5 cm |
SURFACE TREATMENT |
KALENDER AND GAZE PROCESS |
OPERATING TEMPERATURE |
CONTINUOUS 140°C DRY TEMPERATURE |
ACID RESISTANCE |
MIDDLE |
ALKALINE RESISTANCE |
MIDDLE |
HYDROLYSIS RESISTANCE |
PERFECT |
SOLVENT RESISTANCE |
GOOD |
OXID RESISTANCE |
GOOD |